Additive Manufacturing
Additive manufacturing (AM) or additive layer manufacturing (ALM) is the industrial production name for 3D printing, a computer controlled process that creates three dimensional objects by depositing materials, usually in layers.
金属3D打印用粉末材料开发与打印验证
中航迈特拥有一支专业的金属3D打印材料研发团队，在合金粉末材料设计、制备、改性、打印、热处理等方面经验丰富，针对特定应用领域3D打印零件的使用工况，从材料问题入手，研究材料成分、打印工艺及热处理技术，解决行业痛点，帮助用户成长。
GH3536高温合金
| 元素 | C | Cr | Ni | Co | W | Mo | Al | Ti | Fe |
| 标准 | 0.05-0.15 | 20.5-23.0 | 余 | 0.5-2.5 | 0.2-1.0 | 8.0-10.0 | ≤0.5 | ≤0.15 | 17.0-20.0 |
| 实测 | 0.07 | 21.6 | 余 | 1.67 | 0.65 | 8.56 | 0.098 | 0.056 | 18.8 |
| 元素 | B | Si | Mn | P | S | Cu | O | N | |
| 标准 | ≤0.01 | ≤1.00 | ≤1.00 | ≤0.025 | ≤0.015 | ≤0.5 | ≤0.025 | ≤0.015 | |
| 实测 | <0.01 | 0.02 | 0.24 | <0.005 | <0.002 | 0.044 | 0.015 | 0.008 |
机械性能
| 状态 | 室温 | 815℃高温拉伸 | ||
| 抗拉强度 | 延伸率 | 抗拉强度 | 延伸率 | |
| 热处理态 | 730MPa | 36% | 240MPa | 36% |
注：本表打印性能参数为热处理态性能检测数据
CoCrMoW医用合金
| 元素 | Co | Cr | Mo | W | Si | C | Mn |
| 标准 | 余量 | 24.5-28.5 | 4.5-5.5 | 4.0-6.0 | ≤1 | ≤0.3 | ≤1 |
| 实测 | 余量 | 27.5 | 4.92 | 5.14 | 0.4 | 0.003 | ＜0.01 |
机械性能
| 方向 | 状态 | 弯曲强度 | 屈服强度 | 延伸率 | 杨氏模量 | 硬度 | 金瓷结合强度 |
| X向 | 热处理态 | 1025MPa | 665MPa | 18% | 165GPa | 361HV10 | 58MPa |
注：本表打印性能参数为热处理态性能检测数据.
18Ni300模具钢
| 元素 | Co | Ni | Mn | Al | Ti | Si | Mo | O | N |
| 标准 | 8.5-9.5 | 17-19 | ＜0.1 | 0.05-0.15 | 0.6-0.8 | ＜0.1 | 4.5-5.2 | ≤0.03 | ≤0.02 |
| 实测 | 9.01 | 17.95 | 0.07 | 0.08 | 0.67 | 0.01 | 4.76 | 0.028 | 0.010 |
机械性能
| 状态 | 洛氏硬度 | 抗拉强度 | 延伸率 |
| 成形态 | 38.4HRC | 1170MPa | 11.0% |
| 热处理态 | 54.46HRC | 2020MPa | 4.0% |
注：本表打印性能参数为热处理态性能检测数据